After-sales Service: | More Than 5 Years |
---|---|
Warranty: | More Than 5 Years |
Certification: | CE |
Still deciding? Get samples of US$ 0/Piece
Order Sample
|
Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
---|
Payment methods: |
![]() ![]() ![]() ![]() ![]() ![]() ![]() |
---|---|
Support payment in USD |
Secure payments: | Every payment you make at Made-in-china.com is protected by the platform. |
---|
Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
---|
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
S/N |
Item | Index | ||||||
Thickness mm | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | |
1 | Density g/cm3 |
≥0.940 | ||||||
2 | Tensile yield strength (vertical and horizontal) N/mm |
≥11 | ≥15 | ≥18 | ≥22 | ≥29 | ≥37 | ≥44 |
3 | Tensile breaking strength (vertical and horizontal) N/mm |
≥20 | ≥27 | ≥33 | ≥40 | ≥53 | ≥67 | ≥80 |
4 | Elongation (vertical and horizontal) % |
- | - | - | ≥12 | |||
5 | Elongation at break (vertical and horizontal) % |
≥700 | ||||||
6 | Tearing load at right angle (vertical and horizontal) N | ≥93 | ≥125 | ≥160 | ≥190 | ≥250 | ≥315 | ≥375 |
7 | Anti-puncture strength N |
≥240 | ≥320 | ≥400 | ≥480 | ≥540 | ≥800 | ≥960 |
8 ' | Tensile load stress cracking (tensile method of dead load of the cut) h |
_ | ≥300 | |||||
9 | Carbon black content % |
2.0~3.0 | ||||||
10 | Carbon black dispersion | The number of Level 3 among 10 data is not more than one; Level 4 and Level 5 are not allowed. | ||||||
Oxidation induction time (OIT) min |
Oxidation induction time under normal pressure ≥100 | |||||||
11* | Oxidation induction time under disjoining pressure ≥400 | |||||||
12 | 85°C thermal aging (retention rate of OIT under normal pressure after 90d) % | ≥55 | ||||||
13a | Ultraviolet resistance (retention rate of OIT after 1600h ultraviolet irradiation) % |
≥50 | ||||||
Note: Technical performance index of thickness specification not listed in the table shall be implemented according to interpolation method. | ||||||||
For two indexes of Item 11 and Item 13, select one from retention rate of OIT under normal pressure and retention rate of OIT under high pressure and carry out the test. |